Dry-in-place corrosion-resistant coating for zinc or zinc-alloy coated substrates

ABSTRACT

A process for making a corrosion-resistant metal component. The process having the steps of: combining water, at least one zinc phosphate forming compound and at least one chromium forming compound, being chromium (III) or chromium (IV) compounds, to form a first solution; separately combining at least one silicate compound with water to form a second solution; combining the first solution with the second solution such as to form a mixed aqueous solution; optionally combining the mixed aqueous solution with at least one acrylic resin to form a coating mixture; and, applying the coating mixture to the zinc or zinc-alloy surface of the metal substrate forming a covalent bond with the zinc or zinc-alloy surface, and the coating providing chemical resistance for at least 150 hours in accordance with ASTM B117 standards where the zinc or zinc-alloy coating of the metal substrate has a weight of 0.04 oz/ft 2  (12.20 g/m 2 ).

This patent application is a continuation-in-part of U.S. patent application Ser. No. 13/304,822, which was filed on Nov. 28, 2011.

BACKGROUND AND SUMMARY

This invention relates to a process for making a corrosion-resistant coating for zinc or zinc-alloy coated substrates meeting the American Society of Testing and Materials International ASTM B117-11 (hereinafter ASTM B117) standard for continuous salt spray tests of metals and coated metals. The ASTM B117 standard as last amended in August 2011 is incorporated herein by reference.

It is well known that steel rusts when left unprotected in almost any environment. Applying a thin coating of zinc to steel is an effective and economical way to protect steel from corrosion. The most common form of galvanizing metal substrates, either iron, steel or aluminum, is hot-dip galvanizing in which a thick robust layer is deposited on the surface of the metal substrate. The metal substrate is immersed in a bath of molten zinc, at a temperature of about 850° F. (460° C.), to form a metallurgically bonded zinc coating on the metal substrate. The resulting coated metal substrate can be used in much the same way as an uncoated metal substrate.

Coils of steel strip, for example, may be hot-dip galvanized in a continuous line, immersing the steel strip in a molten zinc bath at speeds of up to 600 feet per minute. The specified coating thickness is controlled by air “knives”, which remove the excess coating deposited on the steel as it exits the molten zinc bath. Galvanized steel is used in applications requiring the strength of steel combined with the corrosion resistance of zinc. The continuous galvanizing process can apply a number of different coatings that vary in thickness, appearance, and alloy composition. The term “galvanized” refers to the standard continuous coating having the primary component being zinc. About 0.2% aluminum may be added to the galvanizing bath to form a thin, inhibiting iron-aluminum layer on the steel surface that ensures formation of the zinc coating. The finished zinc or zinc-alloy coating has good formability and corrosion resistance, and provides excellent sacrificial protection. In some applications, the zinc or zinc-alloy coating is applied in conjunction with annealing of the metal substrate, as explained below. These products are often referred to as being galvannealed.

Other processes to galvanize metal substrates include electrodeposition galvanization, otherwise known as electrogalvanization, thermal diffusion galvanizing, and galvannealing. Electrogalvanization comprises immersing a steel substrate in a zinc and saline solution with a zinc anode, the steel substrate acting as the conductor. When electricity is passed through circuit a zinc coating is deposited onto the surface of the steel substrate. In thermal diffusion galvanizing, the metal substrate is tumbled with a mixture of zinc powder and accelerator chemicals, generally sand, and heated to slightly below the melting point of zinc. Galvanized steel results from the combined processes of galvanizing and annealing to produce specialized sheets of steel. To form galvannealed metal substrate, steel is subjected to the hot-dip galvanizing process to form a zinc-coated steel with a very fine grayish matte finish. The coated steel is then heated, to above the recrystallization temperature, maintained at a suitable temperature for a period of time, and then cooled. The heating and cooling alter the properties of the steel, such as strength and ductility. The zinc coating of galvanized steel does not flake off when formed, stamped, and bent. Furthermore, the very fine matte finish acts as a primer, allowing paint to adhere more easily, while affording rust protection. These properties make galvanized steel a popular choice in the automotive, signage and electrical equipment industries.

Zinc coatings protect steel by providing a physical barrier as well as cathodic protection to the underlying steel. The main mechanism by which galvanized coatings protect steel is by providing an impervious barrier that does not allow moisture to contact the steel. Without moisture (the necessary electrolyte), there is no corrosion. When base steel is exposed, e.g., by cutting, scratching or abrading, the exposed steel is still protected by the sacrificial corrosion of the zinc coating adjacent to the exposed steel due to zinc being more electronegative (more reactive) than steel in the galvanic series, causing zinc to oxidize before the steel. Zinc acting as a sacrificial anode is an advantage absent from paint, enamel, powder coatings and other corrosion preventative methods. However, zinc is a reactive metal and will continually corrode slowly over time, eventually losing its protective qualities. Furthermore, in many applications, after a metal substrate has been galvanized the metal substrate is reduced, usually by cold-rolling, but also by hot-rolling, cutting, or abrading, to desired dimensions, reducing the thickness of the zinc-coating and therefore the effectiveness of the corrosion-resistance provided by the zinc-coating. For this reason, there is a need for a corrosion-resistant coating that provides enhanced corrosion protection for zinc or zinc-alloy coated substrates, even when the coated metal substrate having a zinc or zinc-alloy surface has been reduced.

The process herein described may be applicable not only to galvanized steel, but also to galvannealed carbon steel, which is steel which has been coated with zinc, for example, by a hot-dipped process, which converts the coating into a zinc-iron alloy, and subsequently annealed. Conversion to this alloy results in a non-spangle matte finish which makes the sheet suitable for painting after fabrication. Additionally, the present process may be applicable to steel which has been subjected to a Galvalume® process, in which carbon steel sheet is coated with an aluminum-zinc alloy by a continuous hot-dipped process. The nominal coating composition is about 55% aluminum and 45% zinc optionally plus a small addition of silicon (added to at least improve coating adhesion to the steel substrate). This process may be applicable to any form of galvanized metal substrate, including Galvalume® coatings.

The ability of a zinc coating to protect steel depends on zinc's corrosion rate. Freshly exposed galvanized steel reacts with the surrounding atmosphere to form a series of zinc corrosion products (e.g. “white rust” or “red rust”). In air, newly exposed zinc reacts with oxygen to form a very thin zinc oxide layer. When moisture is present, zinc reacts with water resulting in the formation of zinc hydroxide. A common corrosion product to form with exposure to the atmosphere is zinc carbonate as zinc hydroxide reacts with carbon dioxide in the air.

These zinc corrosion products will cause many harmful effects. For example, zinc oxide prevents paint from adhering to the metal as well as accelerates further corrosion of the metal which is unsightly to any galvanized coating's appearance. Pure water contains essentially no dissolved minerals and the zinc will react quickly with pure water to form zinc hydroxide, a bulky white and relatively unstable oxide of zinc. Where freshly galvanized steel is exposed to pure water (e.g., rain, dew or condensation, etc.) particularly in an oxygen-deficient environment, the water will continue to react with the zinc and progressively consume the coating. Therefore, a process for making zinc or zinc-alloy corrosion-resistant metal components with not only exponentially enhanced corrosion-resistance, but also with enhanced adhesion to pre-paints is wanted.

Some commercially available compositions have the capacity to passivate galvanized metal substrates, reducing the formation of zinc corrosion products. These passivators usually utilize a dichromate or chromate composition, typically applied through immersion. Most of these commercially available products provide limited protection to corrosion. An untreated surface will show signs of corrosion after 0.5 hours of exposure to a neutral salt spray according to ASTM specification A1003/A1004, and a thin chromate film produced by a dip procedure will usually show signs of corrosion after 12 to 75 hours of exposure to the salt spray environment. As such, there is a need for a corrosion-resistant coating to provide corrosion resistance exceeding 75 hours of exposure to salt spray environment.

The hot-dip coating process produces many hazardous by-products. For example, when a zinc-phosphate coating is applied to a galvanized metal substrate, via spray coating or dip coating, it must be followed by a rinse step to remove any excess coating composition. The zinc-phosphating rinse water must then be treated to remove any hazardous components. The resultant is a sludge, rich in hazardous components which must be disposed of as hazardous waste according to guidelines set forth by the Environmental Protection Agency (EPA). Sludge also forms in the dipping tanks which must be removed and disposed of according to EPA guidelines. Furthermore, the dipping tanks themselves have a finite lifetime and also must be disposed of according to EPA guidelines. Disposal of hazardous waste is very expensive and time consuming. Therefore, there is presently a need for a coating for a galvanized metal substrate which does not produce hazardous waste by-products which requires laborious and expensive disposal.

The presently disclosed corrosion-resistant coating provides enhanced corrosion resistance to the salt spray environment, that may exceed 1,000 hours of protection for metal substrates having a zinc or zinc-alloy surface coating, and over 144 hours for cold-reduced metal substrates having a zinc or zinc-alloy coating. Furthermore, the presently disclosed corrosion-resistant coating provides for a dry-in-place application, negating the requirement for hazardous waste disposal.

Presently disclosed is a process for making a corrosion-resistant metal component comprising the steps of: combining at least one zinc phosphate forming compound and at least one chromium forming compound with water to form a first solution; separately combining at least one silicate compound with water to form a second solution; combining the first solution with the second solution such as to form a mixed aqueous solution; combining the mixed aqueous solution with at least one acrylic resin to form a coating mixture; and applying the coating mixture to a metal substrate having a zinc or zinc-alloy surface to form a coating on the metal substrate forming a covalent bond with the zinc or zinc-alloy surface of the metal substrate, the coating providing chemical resistance for at least 150 hours in accordance with ASTM B117 standards where the zinc or zinc-alloy surface of the metal substrate has a weight of 0.04 oz/ft² (12.2 g/m²).

The order in which the above-described components are mixed provides a coating with chemical resistance for at least 150 hours in accordance with ASTM B117 standards where the zinc or zinc-alloy surface of the metal substrate has a weight of 0.04 oz/ft² (12.2 g/m²). The order of mixing the components determines the coating composition. The order of mixing the components is key for the reaction between the coating mixture and the zinc or zinc-alloy surface of the metal substrate. The coating mixture reacts in-situ with the zinc or zinc-alloy surface of the metal substrate forming a covalent bond with the zinc or zinc-alloy surface. In the presently claimed invention, covalent bond is defined as the bond formed between the zinc or zinc-alloy substrate forming the zinc phosphate compound, the chromate forming compound, and silicate compound, providing a corrosion resistance of at least 150 hours in accordance with ASTM B117 standards where the zinc or zinc-alloy surface of the metal substrate has a weight of 0.04 oz/ft² (12.2 g/m²). After applying the coating mixture to the metal substrate, the coated metal substrate may be heated to further the reaction between the applied coating mixture and the surface of the metal substrate.

The zinc or zinc-alloy surface may be selected from the group consisting of zinc, zinc alloy, zinc-aluminum alloy, zinc-iron alloy, zinc-aluminum-magnesium alloy and combination thereof. The chromium forming compound may comprise of a trivalent chromium forming compound (i.e. chromium (III)). The trivalent chromium forming compound may be selected from the group consisting of chromium chloride hydrate, chromium (III) potassium sulfate, chromium hydroxide, chromium (III) fluoride, chromium (III) sulfate, chromium (III) sulfide, chromium (III) oxide, chromium (III) 2-ethylhexanoate, chromium (III) nitride, chromium tricarbonyl and mixtures thereof. Alternatively, the chromium forming compound may also comprise of a hexavalent chromium forming compound (i.e chromium (VI)). The hexavalent chromium forming compound may be selected from the group consisting of chromium (VI) halides, hexafluoride, chromyl chloride, sodium chromate, chromium (VI) peroxide, sodium chromate, chromium (VI) oxide, dichromate, potassium chromate, calcium chromate, barium chromate, chromium (VI) oxide peroxide, and mixtures thereof. The at least one silicate compound may comprise a potassium silicate compound.

The first solution may comprise not less than 4 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and balance water. In another embodiment, the first solution may comprise not less than 5 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and balance water. The second solution may comprise not less than 10 and not more than 50 percent by weight of at least one silicate compound, and balance water. The first solution and the second solution may be combined as to form a mixed aqueous solution. The mixed aqueous solution may be combined with at least one acrylic resin to form a coating mixture. The coating mixture may have a pH value of not greater than 2.5. Alternatively, the at least one resin may have a pH value of not greater than 3.5. The coating mixture solution may comprise not less than 20 and not more than 95 percent by weight of the first solution; not less than 5 and not more than 12 percent by weight of the second solution; not less than 5 and not more than 30 percent by weight of the at least one acrylic resin; and balance water.

Also disclosed is a process for making a corrosion-resistant metal component comprising the steps of: combining water, at least one zinc phosphate forming compound and at least one chromium forming compound to form a first solution; separately combining at least one silicate compound with water to form a second solution; combining the first solution with the second solution such as to form a coating mixture; and, applying the coating mixture to a metal substrate having a zinc or zinc-alloy surface to form a coating on the metal substrate forming a covalent bond with the zinc or zinc-alloy substrate, the coating providing chemical resistance for at least 150 hours in accordance with ASTM B117 standards where the zinc or zinc-alloy surface of the metal substrate has a weight of 0.04 oz/ft² (12.2 g/m²).

The coating mixture reacts with the zinc or zinc-alloy surface of the metal substrate forming a covalent bond with the zinc or zinc-alloy surface. After applying the coating mixture to the metal substrate, the coated metal substrate may be heated to further the reaction between the applied coating mixture and the surface of the metal substrate.

The metal substrate may have a zinc or zinc-alloy surface. The zinc or zinc-alloy surface may be selected from the group consisting of zinc, zinc alloy, zinc-aluminum alloy, zinc-iron alloy, zinc-aluminum-magnesium alloy and combination thereof. The at least one chromium forming compound may comprise of a trivalent chromium forming compound (i.e. chromium (III)). The trivalent chromium forming compound may be selected from the group consisting of chromium chloride hydrate, chromium (III) potassium sulfate, chromium hydroxide, chromium (III) fluoride, chromium (III) sulfate, chromium (III) sulfide, chromium (III) oxide, chromium (III) 2-ethylhexanoate, chromium (III) nitride, chromium tricarbonyl and mixtures thereof. Alternatively, the chromium forming compound may comprise of a hexavalent chromium forming compound (i.e. chromium (VI)). The hexavalent chromium forming compound may be selected from the group consisting of chromium (VI) halides, hexafluoride, chromyl chloride, sodium chromate, chromium (VI) peroxide, sodium chromate, chromium (VI) oxide, dichromate, potassium chromate, calcium chromate, barium chromate, chromium (VI) oxide peroxide, and mixtures thereof. The at least one silicate compound may comprise a potassium silicate compound.

The first solution may comprise not less than 4 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and balance water. In another embodiment, the first solution may comprise not less than 5 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and balance water. The second solution may comprise not less than 10 and not more than 50 percent by weight of at least one silicate compound, and balance water. The first solution and the second solution may be combined as to form a coating mixture. The coating mixture may comprise not less than 20 and not more than 95 percent by weight of the first solution; not less than 5 and not more than 12 percent by weight of the second solution; and balance water.

Further disclosed is a process for making a corrosion-resistant metal component coating comprising the steps of: combining water, at least one zinc phosphate forming compound and at least one chromium forming compound to form a first solution; separately combining at least one silicate compound with water to form a second solution; combining the first solution with the second solution such as to form a mixed aqueous solution; and, combining the mixed aqueous solution with at least one acrylic resin to form a corrosion resistant metal component coating mixture for applying to a metal substrate having a zinc or zinc-alloy surface to form a coating on the metal substrate that reacts with the zinc or zinc-alloy surface forming a covalent bond with the zinc or zinc-alloy substrate, the coating providing chemical resistance for at least 150 hours in accordance with ASTM B117 standards where the zinc or zinc-alloy surface of the metal substrate has a weight of 0.04 oz/ft² (12.20 g/m²). In other embodiments, the first solution and the second solution may be combined to form a coating mixture and the coating mixture may be applied to a metal substrate having a zinc or zinc-alloy surface to form a coating on the metal substrate forming a covalent bond with the zinc or zinc-alloy substrate, the coating providing chemical resistance for at least 150 hours in accordance with ASTM B117 standards where the zinc or zinc-alloy surface of the metal substrate has a weight of 0.04 oz/ft² (12.20 g/m²).

The first solution may comprise not less than 4 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and the balance comprising water. In another embodiment, the first solution may comprise not less than 5 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and the balance comprising water. The second solution may comprise not less than 10 and not more than 50 percent by weight of at least one silicate compound, and the balance comprising water. The first solution and the second solution may be combined as to form a mixed aqueous solution. The mixed aqueous solution may be combined with at least one acrylic resin to form a coating mixture. The coating mixture solution may comprise not less than 20 and not more than 95 percent by weight of the first solution; not less than 5 and not more than 12 percent by weight of the second solution; not less than 5 and not more than 30 percent by weight of the at least one acrylic resin; and balance water.

Alternatively, the first solution and the second solution may be combined as to form a coating mixture. The coating mixture may comprise not less than 20 and not more than 95 percent by weight of the first solution; not less than 5 and not more than 12 percent by weight of the second solution; and the balance comprising water.

Regardless, the coating mixture may be applied in various manners such as by rolling the coating mixture onto the metal component surface, by spraying the coating mixture onto the metal component surface, or by submersing at least a portion of the metal substrate with a zinc or zinc-alloy surface into a bath of the coating mixture.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic side-view of an apparatus to provide a dry-in-place application of the presently disclosed corrosion-resistant metal component coating, and a heating apparatus to further the reactive process.

FIG. 2 is a photograph of Hot-Dip Galvanized (HDG) G-60 non-chemically treated (“NCT”) panels exposed to the salt spray environment for up to 120 hours.

FIG. 3 is a photograph of galvannealed panels coated with a solution of the presently disclosed corrosion-resistant metal component coating comprising chromium (VI), exposed to the salt spray environment for up to 1008 hours.

FIG. 4 is a photograph of uncoated galvannealed panels exposed to the salt spray environment for up to 96 hours.

FIG. 5 is a photograph of galvannealed panels, coated with a solution of the presently disclosed corrosion-resistant metal component coating comprising chromium (VI), exposed to the salt spray environment for up to 1512 hours.

FIG. 6 is a photograph of HDG G-40 non-chemically treated (“NCT”) metal substrate panels exposed to salt spray for up to 144 hours.

FIG. 7 is a photograph of metal substrate panels, having a zinc or zinc-alloy surface, coated with a solution of the presently disclosed corrosion-resistant metal component coating comprising chromium (III), cold-reduced by 15% to 23%, and exposed to the salt spray environment for up to 144 hours.

FIG. 8 a is a photograph of the top view of metal substrate panels, having a zinc or zinc-alloy surface, coated with a solution of the presently disclosed corrosion-resistant metal component coating comprising the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds, cold-reduced by 16% to 23%, and exposed to the salt spray environment for up to 120 hours.

FIG. 8 b is a photograph of the bottom view of metal substrate panels, having a zinc or zinc-alloy surface, coated with a solution of the presently disclosed corrosion-resistant metal component coating comprising chromium (VI), cold-reduced by 16% to 23%, and exposed to the salt spray environment for up to 120 hours.

FIG. 9 a is a photograph of the top view of finished formed studs, having a zinc or zinc-alloy surface, coated with a solution of the presently disclosed corrosion-resistant metal component coating comprising chromium (VI), cold-reduced by 16% to 23%, and exposed to the salt spray environment for up to 120 hours.

FIG. 9 b is a photograph of the bottom view of finished formed studs, having a zinc or zinc-alloy surface, coated with a solution of the presently disclosed corrosion-resistant metal component coating comprising chromium (VI), cold-reduced by 16% to 23%, and exposed to salt spray for up to 120 hours.

FIG. 10 is a photograph of uncoated HDG G-40 non-chemically treated (“NCT”) finished formed studs exposed to the salt spray environment for up to 120 hours.

FIG. 11 a is a photograph of the top view of finished formed studs, having a zinc or zinc-alloy surface, coated with a solution of the presently disclosed corrosion-resistant metal component coating comprising chromium (III), cold-reduced by 23% to 24%, and exposed to the salt spray environment for up to 120 hours.

FIG. 11 b is a photograph of the bottom view of finished formed studs, having a zinc or zinc-alloy surface, coated with a solution of the presently disclosed corrosion-resistant metal component coating comprising the presently disclosed corrosion-resistant metal component coating comprising chromium (III) compounds, cold-reduced by 23% to 24%, and exposed to the salt spray environment for up to 120 hours.

FIG. 12 a is a photograph of the top view of finished formed studs, having a zinc or zinc-alloy surface, coated with a solution of the presently disclosed corrosion-resistant metal component coating comprising chromium (VI), cold-reduced by 23% to 24%, and exposed to the salt spray environment for up to 120 hours.

FIG. 12 b is a photograph of the bottom view of finished formed studs, having a zinc or zinc-alloy surface, coated with a solution of the presently disclosed corrosion-resistant metal component coating comprising chromium (VI), cold-reduced by 23% to 24%, and exposed to the salt spray environment for up to 120 hours.

FIG. 13 shows scanning Electron Microscope (SEM) images of the interaction between the presently disclosed corrosion-resistant metal component coating and a zinc or zinc-alloy coated metal substrate surface.

FIG. 14 is a photograph of a metal substrate, having a zinc or zinc-alloy surface, coated with a solution of the presently disclosed corrosion-resistant metal component coating, having water-repellant properties.

DETAILED DESCRIPTION OF THE DRAWINGS

Presently disclosed is a process for making a corrosion-resistant coating for zinc or zinc-alloy coated substrates, and a process for making a corrosion-resistant metal component. Also disclosed is a corrosion-resistant metal component having a corrosion-resistant coating providing chemical resistance.

Referring to FIGS. 2 through 12, uncoated metal substrates having a zinc or zinc-alloy surfaces, and metal substrates having a zinc or zinc-alloy surfaces coated with a solution of the presently disclosed corrosion-resistant metal component coating, comprising chromium (VI) or chromium (III) compounds, were exposed to salt fog environment meeting the requirements of ASTM B117.

The corrosion-resistant coating mixture provides chemical resistance for at least 150 hours in accordance with ASTM B117 standards for a metal substrate having a zinc or zinc-alloy coating weight of 0.04 oz/ft² (12.20 g/m²). The coating mixture provides corrosion resistance for varying periods of time depending on the coating weight of the zinc or zinc-alloy surface of the metal substrate and the coating weight of the corrosion-resistant coating applied to the zinc or zinc-alloy surface of the metal substrate. The phosphate coating component may be a phosphate composition including, for example, phosphoric acid to react with the zinc or zinc-alloy surface of the metal substrate. The metric of chemical resistance for at least 150 hours in accordance with ASTM B117 standards for metal substrate having a zinc or zinc-alloy surface with a coating weight of 0.04 oz/ft² (12.20 g/m²) is a benchmark which provides the effectiveness of the presently disclosed corrosion-resistant coating and process for making a corrosion-resistant component, and it is not a limitation to a particular zinc or zinc-alloy coating weight on a metal substrate. For example, the present process includes a corrosion-resistant coating mixture providing chemical resistance to a metal substrate having a zinc or zinc-alloy surface for at least 75 hours in accordance with ASTM B117 standards where the metal substrate having a zinc or zinc-alloy surface with a coating weight of 0.02 oz/ft² (6.10 g/m²).

The ASTM B117 standard is a widely used standardized salt spray environment cabinet test. Such a salt spray test is used to evaluate the relative corrosive, or chemical, resistance of coated and uncoated materials exposed to a salt spray fog, of 1-2 ml/hr, at an elevated temperature of 95° F. (35° C.). The ASTM B117 standard specifies that specimens are to be placed within an enclosed salt spray cabinet or chamber and subjected to continuous indirect spray of neutral (pH 6.5-7.2) salt water solution. Such a climate may be constantly maintained throughout the salt spray test period. The water used in the salt spray test is compliant with ASTM D1193 Specification for Reagent Water, Type VI. A salt, usually sodium chloride, is added to the water to achieve a solution comprising 5% salt solution. According to ASTM B117 the default position for the specimens within the salt spray chamber is at an angle of 15-30 degrees from the vertical, positioned such that condensation from one specimen will not drip onto another specimen.

Metal substrates having a zinc or zinc-alloy surfaces were coated with the presently disclosed corrosion-resistant metal component coating by the presently disclosed process for making a corrosion-resistant metal component coating comprising the steps of: combining at least one zinc phosphate forming compound and at least one chromium forming compound with water to form a first solution; separately combining at least one silicate compound with water to form a second solution; combining the first solution with the second solution such as to form a coating mixture; and, applying the coating mixture to a metal substrate with a zinc or zinc-alloy surface to form a coating on the metal substrate that reacts with the zinc or zinc-alloy forming a covalent bond with the zinc or zinc-alloy surface to provide a metal substrate with a corrosion-resistant coating mixture providing chemical resistance for at least 150 hours in accordance with ASTM B117 standards for a zinc or zinc-alloy coating weight of 0.04 oz/ft² (12.20 g/m²). In some embodiments the at least one silicate compound may comprise a potassium silicate compound. In further embodiments, the first solution and the second solution may be combined to form a mixed aqueous solution. The mixed aqueous solution may be further combined with at least one acrylic resin to form a coating mixture to be applied to a metal substrate having a zinc or zinc-alloy surface forming a coating on the metal substrate that reacts with the zinc or zinc-alloy forming a covalent bond with the zinc or zinc-alloy surface of the metal substrate to provide a corrosion-resistant coating providing chemical resistance for at least 150 hours in accordance with ASTM B117 standards for a zinc or zinc-alloy coating weight of 0.04 oz/ft² (12.20 g/m²).

Additionally disclosed is a process for making a corrosion-resistant metal component comprising the step of applying a corrosion-resistant coating to a metal substrate having a zinc or zinc-alloy surface to provide a metal component having a corrosion-resistant coating providing a chemical resistance of more than 150 hours in accordance with ASTM B117 standards where the zinc or zinc-alloy coating of the metal substrate has a weight of 0.04 oz/ft² (12.20 g/m²), the corrosion-resistant coating comprising a mixed aqueous solution, the mixed aqueous solution comprising a first solution and a second solution, the first solution comprising water, at least one zinc phosphate forming compound and at least one chromium forming compound, the second solution comprising at least one silicate compound and water. In some embodiments, the corrosion-resistant coating may further comprise at least one acrylic resin.

Furthermore, a corrosion-resistant metal component is disclosed, comprising a metal component having a zinc or zinc-alloy coating; and a corrosion-resistant coating with chemical resistance for more than 150 hours in accordance with ASTM B117 standards where the zinc or zinc-alloy coating of the metal substrate has a weight of 0.04 oz/ft² (12.20 g/m²), wherein the corrosion-resistant coating comprises a first solution and a second solution, wherein the first solution comprises water, at least one zinc phosphate forming compound and at least one chromium forming compound; and wherein the second solution comprises at least one silicate compound and water. In some embodiments, the corrosion-resistant coating may further comprise at least one acrylic resin.

The first solution may comprise between 4 percent and 27 percent by weight of the at least one zinc phosphate forming compound; between 5 percent and 27 percent by weight of chromium forming compound; and balance water. In another embodiment, the first solution may comprise between 5 percent and 27 percent by weight of the at least one zinc phosphate forming compound; between 5 percent and 27 percent by weight of chromium forming compound; and balance water. The second solution may comprise between 10 percent and 50 percent by weight of at least one silicate compound and balance water. The corrosion-resistant metal component coating may comprise between 20 percent and 95 percent by weight of the first solution; between 5 percent and 12 percent by weight of the second solution; between 5 percent and 30 percent by weight of acrylic resin; and balance water. As used in this disclosure, a range specified as between two end points is inclusive of the end points specified.

The first solution may be combined with the second solution to form a mixed aqueous solution. In some embodiments, the mixed aqueous solution may be combined with a least one acrylic resin. In other embodiments, the mixed aqueous solution may not include the acrylic resin. The at least one acrylic resin may have a pH value of no greater than 3.5. Whereas, the corrosion-resistant metal component coating mixture may have a pH value equal to or below 2.5. In some embodiments the coating mixture may have a pH value between 1.0 and 2.5, inclusive. In some embodiments the acrylic resin may be mixed into the aqueous solution in parts adding a first part of the acrylic resin into the aqueous solution and completing the mixing of the acrylic resin into the aqueous solution. The aqueous solution with the first part of acrylic resin may be mixed for a period of time, for example 20 minutes, before a second part of acrylic resin is mixed into the aqueous solution. This process may be repeated until all of the desired amount of acrylic resin is mixed into the aqueous solution. Further, after all of the desired amount of acrylic resin has been mixed into the aqueous solution, the solution may be mixed for a further period of time so that the solution may have an even consistency, making it easier to transport.

The corrosion-resistant metal component coating may comprise at least one chromium forming compound. In some embodiments, the chromium forming compound may comprise of a trivalent chromium forming compound. The trivalent chromium forming compound may be selected from the group consisting of chromium chloride hydrate, chromium (III) potassium sulfate, chromium hydroxide, chromium (III) fluoride, chromium (III) sulfate, chromium (III) sulfide, chromium (III) oxide, chromium (III) 2-ethylhexanoate, chromium (III) nitride, chromium tricarbonyl and mixtures thereof.

In other embodiments, the chromium forming compound may comprise of a hexavalent chromium forming compound. The hexavalent chromium forming compound may be selected from the group consisting of chromium (VI) halides, hexafluoride, chromyl chloride, sodium chromate, chromium (VI) peroxide, sodium chromate, chromium (VI) oxide, dichromate, potassium chromate, calcium chromate, barium chromate, chromium (VI) oxide peroxide, and mixtures thereof.

The corrosion-resistant metal component coating may be applied to a metal component having a zinc or zinc-alloy surface in a number of processes. The coating may be applied through immersion, such that the metal component having a zinc or zinc-alloy surface is immersed into a bath of the presently disclosed corrosion-resistant coating, or the corrosion-resistant coating may be sprayed onto the zinc or zinc-alloy surface of the metal component, with or without the aid of electrolysis. Alternatively, of specific benefit, the presently disclosed corrosion-resistant metal component coating may be applied in a dry-in-place process, as shown in FIG. 1.

Referring to FIG. 1, a coil 8 comprising metal strip component 10 may be provided. The metal component strip 10 having a zinc or zinc-alloy surface 11 is uncoiled from coil 8, and the metal strip component 10 may be transported through the dry-in-place process by a series of strip transfer rolls 16. In the embodiment shown in FIG. 1, the metal strip component 10 passed through an alkaline cleaner 14, where mill surface oils, which may interfere with the reaction between the zinc or zinc-alloy surface 11 of the metal strip component 10 and the presently disclosed corrosion-resistant coating, are removed from the surface of the metal strip component 10 in preparation for receiving the corrosion-resistant coating. The metal strip 10 is then passed, via strip transfer rolls 16 through rinses 15 a and 15 b, neutralizing the pH level of the zinc or zinc-alloy surface 11 of the metal strip 10 after having been passed through the alkaline cleaner 14. The metal strip 10 proceeds via strip transfer rolls 16 through the coater 21. The coater 21 applies the corrosion-resistant metal component coating 20 to the metal strip 10 using reverse-roll coating application method. The coating rolls 12 rotate such that the direction of rotation of the coating rolls opposes the direction of travel of the metal strip 10 proceeding through the coater 21. Corrosion-resistant metal component coating 20 is held in the coating trays 19 and is picked up from the coating trays 19 by pick-up rolls 18. The pick-up rolls 18 and the coating rolls 12 rotate at different velocities, allowing corrosion-resistant metal component coating 20 to be transferred from the pick-up rolls 18 to the coating rolls 12. The speed differential between the coating rolls 12 and the pick-up rolls 18 controls the thickness (coating weight) of the corrosion-resistant metal component coating 20 as it is applied to the strip 10 having a zinc or zinc-alloy surface 11. The rolls 12 may be adapted to coat only one surface 11 of the metal strip component 10, alternatively, as shown in FIG. 1, the rolls 12 may be adapted such that two or more sides of the metal component 10 may be coated simultaneously. In other embodiments, the corrosion-resistant metal component coating may be provided to the rolls 12 through passageways [not shown] in the center of the rolls 12, the passageways having ports 14 allowing the corrosion-resistant coating 15 to travel outward toward the surface of the rolls 12. Alternatively, the corrosion-resistant coating 15 may be applied to the surface of the rolls 12 directly, via an applicator, or sprayed onto the rolls 12.

After the corrosion-resistant metal component coating 20 has been applied to the zinc or zinc-alloy surface 11 of the metal strip component 10, a reaction may occur between the zinc or zinc-alloy surface 11 and the corrosion-resistant coating 20. The process for making a corrosion-resistant metal component may further comprise the step of heating the coated metal substrate 10 to further the reaction between the applied coating mixture 20 and the zinc or zinc-alloy surface 11 of the metal substrate 10. Such heating may be provided by a heating apparatus 17, where the metal substrate 10 is passed, via transfer rolls 16, through the heating apparatus 17 to finalize the reaction. The heating apparatus 17 may be an infra-red heating apparatus capable of heating the surface 11 of the metal component 10. In some embodiments the heating apparatus 17 may heat the surface 11 of the metal component 10 to a temperature of between 170° F.-210° F. In other embodiments, the heating apparatus 17 may heat the surface 11 of the metal component 10 to a higher temperature as desired of up to approximately 700° F. The metal strip component 10 may be passed through the coating applicator rolls 12 and the heating apparatus 17 at a speed of approximately 600 ft/min (3.06 m/s). Finally, the coated metal strip component 10 may be re-coiled into coil 9, for later transportation.

The metal strip component 10 having a zinc or zinc-alloy coating, coated with the corrosion-resistant coating 20 will have comparable electrical conductivity to metal strip 10 having a zinc or zinc-alloy coating, without the corrosion-resistant coating 20. Therefore, the coated galvanize metal substrate provides comparable weldability characteristics as the non-coated galvanized metal substrates.

The metal strip component 10 may be subsequently heated to temperatures of at least 700° F. and maintain the corrosion-resistance necessary to satisfy ASTM A-1004/A-1004M-99 and ASTM A-1003/A-1003M-05 testing standards for galvannealed metal substrates 10, or equivalent standards for other forms of galvanized metal substrates 10, including Galvalumed® metal substrates. The ASTM A-1004/A-1004M-99 and ASTM A-1003/A-1003M-05 testing standards are incorporated herein by reference.

The corrosion resistance of uncoated metal substrates having a zinc or zinc-alloy surface, and metal substrates having a zinc or zinc-alloy surface coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) or chromium (III) compounds was determined following the standards and procedures provided by the American Society of Testing and Materials (ASTM) International. Metal substrates having zinc or zinc-alloy surfaces, coated with or without the presently disclosed corrosion-resistant coating, were exposed to a salt fog environment meeting the requirements of ASTM B117. ASTM B117 provides a controlled corrosive environment which has been utilized to produce relative corrosion resistance information for specimens of metals and coated metals exposed in a given test chamber. All corrosion testing practices were performed in compliance with ASTM A-1004/A-1004M-99 and ASTM A-1003/A-1003M-05. While ASTM A-1004/A-1004M-99 and ASTM A-1003/A-1003M-05 are directed to galvennealed panels, one of ordinary skill in the art will understand that the testing under ASTM A-1004/A-1004M-99 and ASTM A-1003/A-1003M-05 is a benchmark, and will appreciate that the presently disclosed corrosion-resistant metal component coating may be applied to all forms of galvanized metal substrate, including, but not limited to, hot-dipped galvanized, galvannealed, electrogalvanized, and galvalume, and meet or exceed the associated ASTM standards.

In some embodiments, the zinc or zinc-alloy surface is selected from the group consisting of zinc, zinc alloy, zinc-aluminum alloy, zinc-iron alloy, zinc-aluminum-magnesium alloy and combination thereof. According to ASTM A-1003/A-1003M-05, the expected corrosion characteristic for metallic coated sheet steels with nonstructural or non-load-bearing applications is a minimum of 75 hours with less than 10% loss of metallic coating from the surface of the laboratory test samples. The loss of metallic coating from the surface of the laboratory test samples was determined by measuring the percent of red corrosion present after specific times of exposure to the salt spray environment according to ASTM B117.

FIG. 2 shows two HDG G-60 (NCT) panels that have been exposed to the salt spray environment according to ASTM B117 for a period of 120 hours. Referring to FIG. 3, galvannealed metal sheets were exposed to a salt fog environment meeting the requirements of ASTM B117 for periods of 312 hours, 504 hours, 744 hours, and 1008 hours. As illustrated in FIG. 2, the uncoated HDG G-60 (NCT) metal substrate panels showed extensive visible corrosion after 120 hours of exposure to salt spray, presenting red corrosion over 50% of the surface area of the metal substrate panels after 120 hours of exposure to the salt spray environment. FIG. 3 shows four galvannealed panels coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds after being exposed to the salt spray environment for 312 hours, 504 hours, 744 hours and 1008 hours. As illustrated in FIG. 3, the galvannealed panels coated with the presently disclosed corrosion-resistant metal component coating do not show any visible red corrosion after being exposed to the salt spray environment for 1008 hours. Zero percent (0%) of the surface area of all four galvannealed panels coated with the presently disclosed corrosion-resistant coating, presented red corrosion after 1008 hours of exposure to the salt spray environment.

Galvannealed panels coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds, without the optional acrylic resin, from different production runs were also exposed to the salt fog environment meeting the requirements of ASTM B117 for periods of 312 hours, 504 hours, 744 hours, and 1008 hours. Table 1 provides a summary of the percent of surface area of the panels affected by red corrosion for galvannealed panels coated with the presently disclosed corrosion-resistant coating after being exposed to a salt fog environment. All galvannealed panels coated with the corrosion-resistant coating showed zero percent (0%) of surface area affected by red corrosion for up to 1008 hours of exposure to the salt spray environment. Conversely, HDG G-60 (NCT) metal substrate panels showed red corrosion over 50% of their surface area after just 120 hours of exposure to the salt spray environment.

TABLE 1 Galvanneal Panel Set. No. Salt Spray Hours Percent Red Corrosion 1 312 0% 504 0% 744 0% 1008 0% 2 312 0% 504 0% 744 0% 1008 0% 3 312 0% 504 0% 744 0% 1008 0% 4 312 0% 504 0% 744 0% 1008 0% 5 312 0% 504 0% 744 0% 1008 0% Non-chemtreated 120 50%  HDG G-60

In a separate test, galvannealed panels were exposed to a salt fog environment meeting the requirements of ASTM B117 for periods of 504 hours, 744 hours, 1008 hours, 1248 hours, and 1512 hours. As illustrated in FIG. 4, the uncoated A-25 metal substrate panels (galvannealed metal substrate having a zinc or zinc-alloy coating weight of at least 0.25 oz/ft² or 76.29 g/m²) showed extensive visual corrosion after 48 hours of exposure to the salt spray environment. The presence of red corrosion became more visible as the exposure to salt spray increased. The uncoated A-25 metal substrate test panel failed to meet the specifications established by ASTM A-1003/A-1003M by presenting red corrosion over more than 10% of the surface area of the A-25 metal substrate after only 48 hours of exposure to salt spray. FIG. 5 shows five galvannealed panels coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds and acrylic resin after being exposed to salt spray for up to 1512 hours. As illustrated in FIG. 5, none of the galvannealed panels coated with the presently disclosed corrosion-resistant metal component coating comprising acrylic resin showed any visible appearance of red corrosion after being exposed to salt spray for up to 1512 hours. Zero percent (0%) of the surface area of the galvannealed panels coated with the presently disclosed corrosion-resistant coating showed signs of red corrosion. Coating galvannealed metal sheets with the presently disclosed corrosion-resistant metal component coating showed no indication of corrosion when exposed to over 1512 hours of the salt spray environment.

Referring now to FIGS. 6 through 12, the presently disclosed corrosion-resistant metal component coating comprising chromium (III) or chromium (VI) compounds may also be applied to metal substrates, having a zinc or zinc-alloy surface, that are to be cold-reduced and provide enhanced corrosion protection after the reducing process. After being coated with the presently disclosed corrosion-resistant coating, the zinc or zinc-alloy coated panels were reduced and exposed to a salt fog environment meeting the standards of ASTM B117. Referring to FIG. 7, metal panels, having a zinc or zinc-alloy surface, were coated with the presently disclosed corrosion-resistant coating comprising acrylic resin, cold-reduced by 15% to 23%, and were exposed to a salt fog for periods of 48 hours, 75 hours, 96 hours, 120 hours, and 144 hours. As illustrated in FIG. 6, the HDG G-40 (NCT) metal substrate panels showed visual corrosion after 75 hours of exposure to the salt spray environment. Red corrosion became more visible as the exposure to the salt spray environment increased. The standard HDG G-40 (NCT) metal substrate panels showed 1%, 25%, 50%, and 75% of surface area affected by red corrosion after 72 hours, 96 hours, 120 hours, and 144 hours of exposure to the salt spray environment, respectively. FIG. 7 shows metal panels, having a zinc or zinc-alloy surface, which have been coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (III) compounds and acrylic resin and then cold-reduced by 15% to 23%. The coated galvanized panels were then subjected to 48 hours, 75 hours, 96 hours, 120 hours, and 144 hours of salt spray testing. Zero percent (0%) of the surface area of the cold-reduced coated galvanized panels were affected by red corrosion.

Table 2 provides a summary of tests performed, showing the percent of red corrosion for zinc-alloy coated panels coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (III) compounds and acrylic resin, having been cold-reduced after coating by 15% to 23% and exposed to a salt fog environment meeting the requirements of ASTM B117, for periods of 48 hours, 75 hours, 96 hours, 120 hours, and 144 hours. All zinc-alloy coated panels, coated with the presently disclosed corrosion-resistant metal component coating, and reduced after coating by 15% to 23%, showed zero percent (0%) surface area of the panels affected by red corrosion after being exposed to salt spray for up to 120 hours. The panels, having a zinc or zinc-alloy surface, coated with the presently disclosed corrosion-resistant metal component coating, and cold-reduced after coating by 15% to 23% exceeded the ASTM A-1003/A-1003M standards by presenting less than three percent (3%) of red corrosion after 144 hours of exposure to the salt spray environment. The zinc-alloy coated panels coated with the presently disclosed corrosion-resistant metal component coating, and cold-reduced by 15% to 23% showed complete resistance to corrosion for up to 120 hours of salt spray, and red rust over less than 3% of the surface area at 144 hours salt spray compared to red corrosion over 75% of the surface area of the HDG G-40 (NCT) panels after 144 hours of exposure to the salt spray environment.

TABLE 2 Galvanneal Metal Substrate Cold-Reduced by 15-23% Set. No. Salt Spray Hours Percent Red Corrosion 1 48 0% chromium (III) 75 0% with acrylic resin 96 0% 120 0% 144 <3%  2 48 0% chromium (III) 75 0% with acrylic resin 96 0% 120 0% 144 <3%  3 48 0% chromium (III) 75 0% with acrylic resin 96 0% 120 0% 144 <3%  Non-chemtreated 72 1% HDG G-40 96 25%  120 50%  144 75% 

Referring to FIGS. 8 a-b, zinc or zinc-alloy coated panels were cold-reduced by 16% to 23% after being coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds and acrylic resin. Uncoated zinc or zinc-alloy coated panels were exposed to a salt fog environment meeting the requirements of ASTM B117 for periods of 48 hours, 75 hours, 96 hours, and 120 hours. As illustrated in FIG. 6, the HDG G-40 (NCT) metal substrate panels showed visual corrosion after 48 hours of exposure to the salt spray environment. Red corrosion became more visible as the exposure to the salt spray environment increased. The HDG G-40 (NCT) metal substrate panels showed 5%, 10%, 25%, and 50% of red corrosion after 48 hours, 75 hours, 96 hours, and 120 hours of salt spray exposure, respectively. FIG. 8 a shows the top view of zinc-alloy coated metal panels coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds and cold-reduced after coating by 16% to 23% and then exposed to salt spray for 48 hours, 75 hours, 96 hours, and 120 hours. FIG. 8 b, shows the bottom view of zinc-alloy coated panels coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds and cold-reduced after coating by 16% to 23% and exposed to salt spray for 48 hours, 75 hours, 96 hours, and 120 hours. Zero percent (0%) of the surface area of the zinc-alloy coated metal panels coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (III) compounds and cold-reduced after coating by 16% to 23%, showed signs of red corrosion.

Zinc-alloy panels coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds and cold-reduced after coating by 16% to 23% from different production runs were exposed to the salt fog environment. Table 3 provides a summary of the percent of surface area affected by red corrosion for zinc-alloy coated panels coated with the presently disclosed corrosion-resistant metal component coating, and cold-reduced after coating by 16% to 23% and exposed to the salt fog environment meeting the requirements of ASTM B117, for periods of 48 hours, 75 hours, 96 hours, and 120 hours. All zinc-alloy panels that were coated with the presently disclosed corrosion-resistant metal component coating, and were cold-reduced after coating by 16% to 23% showed zero percent (0%) of surface area affected by red corrosion. The zinc-alloy panels coated with the presently disclosed corrosion-resistant metal component coating, and cold-reduced by 16% to 23% showed no indication of corrosion for up to 120 hours of the salt spray exposure, compared with the HDG G-40 (NCT), which presented 50% of red corrosion after 120 hours of the salt spray exposure.

TABLE 3 Metal Substrate Cold- Reduced by 16-23% Set No. Salt Spray Hours Percent Red Corrosion 1 48 0% chromium (IV) 75 0% with acrylic resin 96 0% 120 0% 2 48 0% chromium (IV) 75 0% with acrylic resin 96 0% 120 0% 3 48 0% chromium (IV) 75 0% with acrylic resin 96 0% 120 0% Non-chemtreated HDG G-40 48 −5%  75 10%  96 25%  120 50% 

FIGS. 9 a-b show finished formed studs, having a zinc-alloy surface, coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds and cold-reduced after coating by 16% to 23% were exposed to a salt fog environment meeting the requirements of ASTM B117 for periods of 75 hours, 96 hours, and 120 hours. As illustrated in FIG. 9 a, the top part of the finished formed studs, having a zinc-alloy surface, coated with the presently disclosed corrosion-resistant metal component coating, and cold-reduced after coating by 16% to 23% showed zero percent (0%) of surface area affected by red corrosion after being exposed to the salt spray environment for 75 hours, 96 hours, and 120 hours. Similarly, FIG. 9 b shows the bottom part of the finished formed studs, having a zinc-alloy surface, coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds and cold-reduced after coating by 16% to 23%. Zero percent (0%) of the surface area of the finished formed studs, having a zinc-alloy surface, coated with the presently disclosed corrosion-resistant coating, cold-reduced, and exposed to the salt fog environment for up to 120 hours, showed signs of red corrosion.

FIGS. 10 through 12 illustrate metal substrates having a zinc or zinc-alloy surface, coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (III) or chromium (VI) compounds, cold-reduced by 23% to 24% after coating and subject to the salt spray testing environment. As shown by FIGS. 10 and 11 a-b, finished formed studs of zinc-alloy coated metal substrate coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (III) compounds, cold-reduced by 23% to 24% after coating and exposed to the salt fog environment, meeting the requirements of ASTM B117, for periods of 75 hours, 96 hours, and 120 hours. FIG. 10 shows HDG G-40 (NCT) finished formed studs having been subjected to the salt spray testing environment for up to 120 hours. The HDG G-40 (NCT) finished formed studs showed visual corrosion after 96 hours of exposure to the salt spray environment. The HDG G-40 (NCT) finished formed studs presented 5% and 25% of red corrosion after 96 hours and 120 hours of salt spray environment exposure, respectively. As illustrated by FIGS. 11 a-b, finished formed studs made with zinc-alloy coated metal substrate coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (III) compounds and cold-reduced by 23% to 24% after coating have enhanced corrosion resistance. As seen in FIGS. 11 a and 11 b, both top and bottom views of the finished formed studs, having a zinc-alloy surface, coated with the presently disclosed corrosion-resistant metal component coating presented zero percent (0%) of surface area affected by red corrosion after being exposed to salt spray for 75 hours, 96 hours, and 120 hours.

Similarly, metal substrates having a zinc or zinc-alloy surface were coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds, cold-reduced by 23% to 24% and subjected to salt spray testing. FIGS. 12 a-b illustrate finished formed studs, having a zinc-alloy surface, coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds, cold-reduced by 23% to 24% after coating, and exposed to the salt fog environment meeting the requirements of ASTM B117, for periods of 75 hours, 96 hours, and 120 hours. As illustrated in FIGS. 12 a and 12 b, both top and bottom views of the finished formed studs, having a zinc-alloy surface, coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds present zero percent (0%) of their surface area affected by red corrosion after being exposed to the salt spray environment for of 75 hours, 96 hours, and 120 hours.

The effectiveness of the presently disclosed corrosion-resistant metal component coating comprising chromium (III) or chromium (VI) compounds to protect galvanized metal substrates, such as hot-dip galvanized metal substrates or galvannealed metal substrates, from corrosion is dependent upon the thickness of the zinc or zinc-alloy coating and the thickness of the presently disclosed corrosion-resistant metal component coating. Table 4 provides a summary of the number hours achieved under the salt spray testing environment with less than ten percent (10%) of weight loss for HDG G-30 metal substrates coated with the presently disclosed corrosion-resistant metal component coating. Over 1000 hours of corrosion-free salt spray environment testing were obtained for galvanized metal coated with the presently disclosed corrosion-resistant metal component coating, with a coating weight of at least 0.0106 oz/ft² (3.23 g/m²). Over 500 hours of corrosion-free salt spray testing was obtained for galvanized metal substrates coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds to a coating weight of at least 0.0053 oz/ft² (1.61 g/m²). And, over 500 hours of corrosion-free salt spray environment testing were obtained for galvanized metal substrates coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (III) compounds to a coating weight of at least 0.0053 oz/ft² (1.61 g/m²).

TABLE 4 Salt spray hours Chromium Coating weight achieved with less Metal substrate compound (oz/ft²); (g/m²) than 10% weight loss Galvanized Chromium (VI) 0.0106-0.0132 1000 hours+ G-30 (3.229-4.036) Chromium (III) 0.0106-0.0127 1000 hours+ (3.229-3.875) Chromium (VI) 0.0053-0.0071  500 hours+ (1.615-2.153) Chromium (III) 0.0053-0.0071  500 hours+ (1.615-2.153)

Similarly, the effectiveness of the presently disclosed corrosion-resistant metal component coating comprising chromium (III) or chromium (VI) compounds to protect galvannealed metal substrates from corrosion is dependent upon the coating thickness of the presently disclosed corrosion-resistant metal component coating. Table 5 provides a summary of the number of hours of salt spray testing achieved with less than ten percent (10%) of weight loss after exposing galvannealed A-25 or A-40 metal substrates coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (III) or chromium (VI) compounds to a salt fog environment meeting the requirements of ASTM B117. Over 1000 hours of salt spray testing were obtained for galvannealed metal substrate coated with the presently disclosed corrosion-resistant metal component coating comprising having a coating weight of at least 0.0106 oz/ft² (3.23 g/m²), while maintaining less than 10% red corrosion on the surface of the metal substrate. Whereas, over 500 hours of salt spray testing were obtained for galvannealed metal substrates coated with presently disclosed corrosion-resistant metal component coating comprising chromium (VI) compounds to a coating weight of at least 0.0053 oz/ft² (1.61 g/m²), while maintaining less than 10% red corrosion on the surface of the metal substrate. And, over 500 hours of salt spray environment testing were obtained for galvannealed metal substrates coated with presently disclosed corrosion-resistant metal component coating comprising chromium (III) compounds to a coating weight of at least 0.0053 mg/ft² (1.61 g/m²), while maintaining less than 10% red corrosion on the surface of the metal substrate.

TABLE 5 Salt spray hours Chromium Coating weight achieved with less Metal substrate compound (oz/ft²); (g/m²) than 10% weight loss Galvannealed Chromium (VI) 0.0106-0.0132 1000 hours+ A-25 or A-40 (3.229-4.036) Chromium (III) 0.0106-0.0127 1000 hours+ (3.229-3.875) Chromium (VI) 0.0053-0.0071  500 hours+ (1.615-2.153) Chromium (III) 0.0053-0.0071  500 hours+ (1.615-2.153)

As illustrated in FIGS. 2 through 12, the application of the presently disclosed corrosion-resistant metal component coating, comprising chromium (III) or chromium (VI) compounds, to the metal substrates having a zinc or zinc-alloy surface, significantly enhances the ability of the metal substrate to resist corrosion. The presently disclosed corrosion-resistant metal component coating interacts with the zinc or zinc-alloy coated metal substrate. The Scanning Electron Microscope (SEM) images in FIG. 13 show the reaction between the presently disclosed corrosion-resistant metal component coating and the zinc or zinc-alloy surface of the metal substrate. Such a reaction forms a covalent bond, as defined herein between the presently disclosed corrosion-resistant coating and the zinc or zinc-alloy surface. The SEM images show the imperfections (i.e. fractures and/or porosity) that exist in zinc or zinc-alloy surface. When the presently disclosed corrosion-resistant metal component coating is applied to a zinc or zinc-alloy surface of the metal substrate, the coating mixture may penetrate down into any deep cracks and voids in the zinc coating. The reaction between the corrosion-resistant metal component coating and the zinc or zinc-alloy surface of the metal substrate may seal off exterior corrosion sources and protect the zinc layer as well as the carbon steel base metal.

In one embodiment, the coating mixture may be applied by rolling the coating mixture onto the metal component surface. This direct mode of application may decrease the amount of residual coating mixture. In another embodiment, the coating mixture may be applied by spraying the coating mixture onto the metal component surface, or alternatively, the coating mixture may be applied by submersing at least a portion of the metal substrate with a zinc or zinc-alloy surface into a bath of the presently disclosed corrosion-resistant metal component coating.

As illustrated in FIG. 14, the metal substrates having a zinc or zinc-alloy surface and coated with the presently disclosed corrosion-resistant metal component coating comprising chromium (III) or chromium (VI) compounds may be water-repellant. Water-repellency provides extra protection for the zinc or zinc-alloy substrate against corrosion. In air, newly exposed zinc reacts with oxygen to form a very thin zinc oxide layer. When moisture is present, zinc reacts with water resulting in the formation of zinc hydroxide, when dry, this becomes zinc oxide. Zinc oxide prevents paint from adhering to the metal as well as accelerates further corrosion of the metal which is unsightly to any galvanized coating's appearance. Furthermore, pure water contains essentially no dissolved minerals and the zinc will react quickly with pure water to form zinc hydroxide, a bulky white and relatively unstable oxide of inc. Where freshly galvanized steel is exposed to pure water (e.g., rain, dew or condensation, etc.) particularly in an oxygen-deficient environment, the water may continue to react with the zinc and progressively consume the zinc or zinc-alloy coating.

The presently disclosed corrosion-resistant coating may be self-healing. The coating protecting a metal substrate from corrosion may protect the metal substrate even if the metal substrate is cut, scratched or abraded. For example, a metal substrate may become scratched when being cold-rolled using rollers which have surface defects imparting scratches onto the surface of the molten metal. Scratching of the metal substrate may remove the corrosion-resistant coating from that portion, exposing the metal substrate. It is desirable that a corrosion-resistant coating will protect the exposed portion of the metal substrate. One such method of protection is to provide sufficient corrosion-resistant coating material that part of the coating may remain non-reacted with the zinc or zinc-alloy surface. The non-reacted coating may then react with the scratched, exposed, portion of the metal substrate forming a protective coating over it. Thus, the corrosion-resistant coating is self-healing.

While the principle and mode of operation of this invention have been explained and illustrated with regard to particular embodiments, it must be understood; however, that this invention may be practiced otherwise than as specifically explained and illustrated without departing from its spirit or scope. Therefore, it is intended that the invention not be limited to the particular embodiments falling within the scope of the appended claims. 

1. A process for making a corrosion-resistant metal component comprising the steps of: combining water, at least one zinc phosphate forming compound and at least one chromium forming compound to form a first solution; separately combining at least one silicate compound with water to form a second solution; combining the first solution with the second solution such as to form a mixed aqueous solution; combining the mixed aqueous solution with at least one acrylic resin to form a coating mixture; and applying the coating mixture to a metal substrate having a zinc or zinc-alloy surface to form a coating on the metal substrate that reacts with the zinc or zinc-alloy surface of the metal substrate forming a covalent bond with the zinc or zinc-alloy surface, and the coating providing chemical resistance for at least 150 hours in accordance with ASTM B117 standards where the zinc or zinc-alloy coating of the metal substrate has a weight of 0.04 oz/ft² (12.20 g/m²).
 2. A process for making a corrosion-resistant metal component as claimed in claim 1, further comprising the step of heating the coated metal substrate to further the reaction between the applied coating mixture and the surface of the metal substrate.
 3. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the zinc or zinc-alloy surface is selected from the group consisting of zinc, zinc alloy, zinc-aluminum alloy, zinc-iron alloy, zinc-aluminum-magnesium alloy and combinations thereof.
 4. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the first solution comprises: not less than 4 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and balance water.
 5. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the first solution comprises: not less than 5 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and balance water.
 6. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the second solution comprises: not less than 10 and not more than 50 percent by weight of at least one silicate compound; and balance water.
 7. A process for making a corrosion-resistant metal component as claimed in claim 1, wherein the coating mixture comprises: not less than 20 and not more than 95 percent by weight of the first solution; not less than 5 and not more than 12 percent by weight of the second solution; not less than 5 and not more than 30 percent by weight of the at least one acrylic resin; and balance water.
 8. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the at least one acrylic resin has a pH value of no greater than 3.5.
 9. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the at least the coating mixture has a pH value of no greater than 2.5.
 10. A process for making a corrosion-resistant metal component as claimed in 1 wherein the at least one silicate compound comprises a potassium silicate compound.
 11. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the at least one chromium forming compound comprises a trivalent chromium forming compound.
 12. A process for making a corrosion-resistant metal component as claimed in claim 11 wherein the trivalent chromium forming compound is selected from the group consisting of chromium chloride hydrate, chromium (III) potassium sulfate, chromium hydroxide, chromium (III) fluoride, chromium (III) sulfate, chromium (III) sulfide, chromium (III) oxide, chromium (III) 2-ethylhexanoate, chromium (III) nitride, chromium tricarbonyl and mixtures thereof.
 13. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the at least one chromium forming compound comprises a hexavalent chromium forming compound.
 14. A process for making a corrosion-resistant metal component as claimed in claim 13 wherein the hexavalent chromium forming compound is selected from the group consisting of chromium (VI) halides, hexafluoride, chromyl chloride, sodium chromate, chromium (VI) peroxide, sodium chromate, chromium (VI) oxide, dichromate, potassium chromate, calcium chromate, barium chromate, chromium (VI) oxide peroxide, and mixtures thereof.
 15. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the step of applying the coating mixture comprises rolling the coating mixture onto the metal component surface.
 16. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the step of applying the coating mixture comprises spraying the coating mixture onto the metal component surface.
 17. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the step of applying the coating mixture comprises submersing at least a portion of the metal substrate with a zinc or zinc-alloy surface into a bath of the coating mixture.
 18. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the step of applying the coating mixture solution further comprises filling any voids in the zinc or zinc-alloy surface with the coating mixture solution.
 19. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the coating provides electrical conductivity.
 20. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the coating is water-repellant.
 21. A process for making a corrosion-resistant metal component as claimed in claim 1 wherein the coating provides an enhanced surface for a zinc or zinc-alloy coated metal component for adhesion to paints.
 22. A process for making a corrosion-resistant metal component coating as claimed in claim 1 wherein the coating is self-healing.
 23. A process for making a corrosion-resistant metal component comprising the steps of: combining water, at least one zinc phosphate forming compound and at least one chromium forming compound to form a first solution; separately combining at least one silicate compound with water to form a second solution; combining the first solution with the second solution such as to form a coating mixture; and applying the coating mixture to a metal substrate having a zinc or zinc-alloy surface to form a coating on the metal substrate that reacts with the zinc or zinc-alloy surface of the metal substrate forming a covalent bond with the zinc or zinc-alloy surface, and the coating providing chemical resistance for at least 150 hours in accordance with ASTM B117 standards where the zinc or zinc-alloy coating of the metal substrate has a weight of 0.04 oz/ft² (12.20 g/m²).
 24. A process for making a corrosion-resistant metal component as claimed in claim 23, further comprising the step of heating the coated metal substrate to further the reaction between the applied coating mixture and the surface of the substrate.
 25. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the zinc or zinc-alloy surface is selected from the group consisting of zinc, zinc alloy, zinc-aluminum alloy, zinc-iron alloy, zinc-aluminum-magnesium alloy and combinations thereof.
 26. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the first solution comprises: not less than 4 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and balance water.
 27. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the first solution comprises: not less than 5 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and balance water.
 28. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the second solution comprises: not less than 10 and not more than 50 percent by weight of at least one silicate compound; and balance water.
 29. A process for making a corrosion-resistant metal component as claimed in claim 23, wherein the coating mixture comprises: not less than 20 and not more than 95 percent by weight of the first solution; not less than 5 and not more than 12 percent by weight of the second solution; and balance water.
 30. A process for making a corrosion-resistant metal component as claimed in 23 wherein the at least one silicate compound comprises a potassium silicate compound.
 31. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the coating mixture has a pH value of no greater than 2.5.
 32. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the at least one chromium forming compound comprises a trivalent chromium forming compound.
 33. A process for making a corrosion-resistant metal component as claimed in claim 32 wherein the trivalent chromium forming compound is selected from the group consisting of chromium chloride hydrate, chromium (III) potassium sulfate, chromium hydroxide, chromium (III) fluoride, chromium (III) sulfate, chromium (III) sulfide, chromium (III) oxide, chromium (III) 2-ethylhexanoate, chromium (III) nitride, chromium tricarbonyl and mixtures thereof.
 34. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the at least one chromium forming compound comprises a hexavalent chromium forming compound.
 35. A process for making a corrosion-resistant metal component as claimed in claim 34 wherein the hexavalent chromium forming compound is selected from the group consisting of chromium (VI) halides, hexafluoride, chromyl chloride, sodium chromate, chromium (VI) peroxide, sodium chromate, chromium (VI) oxide, dichromate, potassium chromate, calcium chromate, barium chromate, chromium (VI) oxide peroxide, and mixtures thereof.
 36. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the step of applying the coating mixture comprises rolling the coating mixture onto the metal component surface.
 37. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the step of applying the coating mixture comprises spraying the coating mixture onto the metal component surface.
 38. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the step of applying the coating mixture comprises submersing at least a portion of the metal substrate with a zinc or zinc-alloy surface into a bath of the coating mixture.
 39. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the step of applying the coating mixture solution further comprises filling any voids in the zinc or zinc-alloy surface with the coating mixture solution.
 40. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the coating provides electrical conductivity.
 41. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the coating is water-repellant.
 42. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the coating provides an enhanced surface for a zinc or zinc-alloy coated metal component for adhesion to paints.
 43. A process for making a corrosion-resistant metal component as claimed in claim 23 wherein the coating is self-healing.
 44. A process for making a corrosion-resistant metal component coating comprising the steps of: combining water, at least one zinc phosphate forming compound and at least one chromium forming compound to form a first solution; separately combining at least one silicate compound with water to form a second solution; combining the first solution with the second solution such as to form a mixed aqueous solution; combining the mixed aqueous solution with at least one acrylic resin to form a coating mixture; and applying the coating mixture to a metal substrate having a zinc or zinc-alloy surface to form a coating on the metal substrate that reacts with the zinc or zinc-alloy surface of the metal substrate forming a covalent bond with the zinc or zinc-alloy surface, and the coating providing chemical resistance for at least 150 hours in accordance with ASTM B117 standards where the zinc or zinc-alloy coating of the metal substrate has a weight of 0.04 oz/ft² (12.20 g/m²).
 45. A process for making a corrosion-resistant metal component coating as claimed in claim 44, further comprising the step of heating the coated metal substrate to further the reaction between the applied coating mixture and the surface of the metal substrate.
 46. A process for making a corrosion-resistant metal component coating as claimed in claim 44, wherein the zinc or zinc-alloy surface is selected from the group consisting of zinc, zinc alloy, zinc-aluminum alloy, zinc-iron alloy, zinc-aluminum-magnesium alloy and combinations thereof.
 47. A process for making a corrosion-resistant metal component coating as claimed in claim 44, wherein the first solution comprises: not less than 4 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and balance water.
 48. A process for making a corrosion-resistant metal component coating as claimed in claim 44, wherein the first solution comprises: not less than 5 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and balance water.
 49. A process for making a corrosion-resistant metal component coating as claimed in claim 44 wherein the second solution comprises: not less than 10 and not more than 50 percent by weight of at least one silicate compound; and balance water.
 50. A process for making a corrosion-resistant metal component coating as claimed in claim 44, wherein the coating mixture comprises: not less than 20 and not more than 95 percent by weight of the first solution; not less than 5 and not more than 12 percent by weight of the second solution; not less than 5 and not more than 30 percent by weight of the at least one acrylic resin; and balance water.
 51. A process for making a corrosion-resistant metal component coating as claimed in claim 44 wherein the at least one acrylic resin has a pH value of no greater than 3.5.
 52. A process for making a corrosion-resistant metal component coating as claimed in claim 44 wherein the coating mixture has a pH value of no greater than 2.5.
 53. A process for making a corrosion-resistant metal component coating as claimed in 44 wherein the at least one silicate compound comprises a potassium silicate compound.
 54. A process for making a corrosion-resistant metal component coating as claimed in claim 44 wherein the at least one chromium forming compound comprises a trivalent chromium forming compound.
 55. A process for making a corrosion-resistant metal component coating as claimed in claim 54 wherein the trivalent chromium forming compound is selected from the group consisting of chromium chloride hydrate, chromium (III) potassium sulfate, chromium hydroxide, chromium (III) fluoride, chromium (III) sulfate, chromium (III) sulfide, chromium (III) oxide, chromium (III) 2-ethylhexanoate, chromium (III) nitride, chromium tricarbonyl and mixtures thereof.
 56. A process for making a corrosion-resistant metal component coating as claimed in claim 44 wherein the at least one chromium forming compound comprises a hexavalent chromium forming compound.
 57. A process for making a corrosion-resistant metal component coating as claimed in claim 56 wherein the hexavalent chromium forming compound is selected from the group consisting of chromium (VI) halides, hexafluoride, chromyl chloride, sodium chromate, chromium (VI) peroxide, sodium chromate, chromium (VI) oxide, dichromate, potassium chromate, calcium chromate, barium chromate, chromium (VI) oxide peroxide, and mixtures thereof.
 58. A process for making a corrosion-resistant metal component coating as claimed in claim 44 wherein the step of applying the coating mixture comprises rolling the coating mixture onto the metal component surface.
 59. A process for making a corrosion-resistant metal component coating as claimed in claim 44 wherein the step of applying the coating mixture comprises spraying the coating mixture onto the metal component surface.
 60. A process for making a corrosion-resistant metal component coating as claimed in claim 44 wherein the step of applying the coating mixture comprises submersing at least a portion of the metal substrate with a zinc or zinc-alloy surface into a bath of the coating mixture.
 61. A process for making a corrosion-resistant metal component coating as claimed in claim 44 wherein the step of applying the coating mixture solution further comprises filling any voids in the zinc or zinc-alloy surface with the coating mixture solution.
 62. A process for making a corrosion-resistant metal component coating as claimed in claim 44 wherein the corrosion-resistant metal component coating provides electrical conductivity.
 63. A process for making a corrosion-resistant metal component coating as claimed in claim 44 wherein the corrosion-resistant metal component coating is water-repellant.
 64. A process for making a corrosion-resistant metal component coating as claimed in claim 44 wherein the corrosion-resistant metal component coating provides an enhanced surface for a zinc or zinc-alloy coated metal component for adhesion to paints.
 65. A process for making a corrosion-resistant metal component coating as claimed in claim 44 wherein the corrosion-resistant metal component coating is self-healing.
 66. A process for making a corrosion-resistant metal component coating comprising the steps of: combining water, at least one zinc phosphate forming compound and at least one chromium forming compound to form a first solution; separately combining at least one silicate compound with water to form a second solution; combining the first solution with the second solution such as to form a coating mixture; and applying the coating mixture to a metal substrate having a zinc or zinc-alloy surface to form a coating on the metal substrate that reacts with the zinc or zinc-alloy surface of the metal substrate forming a covalent bond with the zinc or zinc-alloy surface, and the coating providing chemical resistance for at least 150 hours in accordance with ASTM B117 standards where the zinc or zinc-alloy coating of the metal substrate has a weight of 0.04 oz/ft² (12.20 g/m²).
 67. A process for making a corrosion-resistant metal component coating as claimed in claim 66, further comprising the step of heating the coated metal substrate to further the reaction between the applied coating mixture and the surface of the metal substrate.
 68. A process for making a corrosion-resistant metal component coating as claimed in claim 66, wherein the zinc or zinc-alloy surface is selected from the group consisting of zinc, zinc alloy, zinc-aluminum alloy, zinc-iron alloy, zinc-aluminum-magnesium alloy and combinations thereof.
 69. A process for making a corrosion-resistant metal component coating as claimed in claim 66, wherein the first solution comprises: not less than 4 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and balance water.
 70. A process for making a corrosion-resistant metal component coating as claimed in claim 66, wherein the first solution comprises: not less than 5 and not more than 27 percent by weight of the at least one zinc phosphate forming compound; not less than 5 and not more than 27 percent by weight of the at least one chromium forming compound; and balance water.
 71. A process for making a corrosion-resistant metal component coating as claimed in claim 66 wherein the second solution comprises: not less than 10 and not more than 50 percent by weight of at least one silicate compound; and balance water.
 72. A process for making a corrosion-resistant metal component coating as claimed in claim 66, wherein the coating mixture comprises: not less than 20 and not more than 95 percent by weight of the first solution; not less than 5 and not more than 12 percent by weight of the second solution; and balance water.
 73. A process for making a corrosion-resistant metal component coating as claimed in claim 66 wherein the coating mixture has a pH value of no greater than 2.5.
 74. A process for making a corrosion-resistant metal component coating as claimed in 66 wherein the at least one silicate compound comprises a potassium silicate compound.
 75. A process for making a corrosion-resistant metal component coating as claimed in claim 66 wherein the at least one chromium forming compound comprises a trivalent chromium forming compound.
 76. A process for making a corrosion-resistant metal component coating as claimed in claim 75 wherein the trivalent chromium forming compound is selected from the group consisting of chromium chloride hydrate, chromium (III) potassium sulfate, chromium hydroxide, chromium (III) fluoride, chromium (III) sulfate, chromium (III) sulfide, chromium (III) oxide, chromium (III) 2-ethylhexanoate, chromium (III) nitride, chromium tricarbonyl and mixtures thereof.
 77. A process for making a corrosion-resistant metal component coating as claimed in claim 66 wherein the at least one chromium forming compound comprises a hexavalent chromium forming compound.
 78. A process for making a corrosion-resistant metal component coating as claimed in claim 77 wherein the hexavalent chromium forming compound is selected from the group consisting of chromium (VI) halides, hexafluoride, chromyl chloride, sodium chromate, chromium (VI) peroxide, sodium chromate, chromium (VI) oxide, dichromate, potassium chromate, calcium chromate, barium chromate, chromium (VI) oxide peroxide, and mixtures thereof.
 79. A process for making a corrosion-resistant metal component coating as claimed in claim 66 wherein the step of applying the coating mixture comprises rolling the coating mixture onto the metal component surface.
 80. A process for making a corrosion-resistant metal component coating as claimed in claim 66 wherein the step of applying the coating mixture comprises spraying the coating mixture onto the metal component surface.
 81. A process for making a corrosion-resistant metal component coating as claimed in claim 66 wherein the step of applying the coating mixture comprises submersing at least a portion of the metal substrate with a zinc or zinc-alloy surface into a bath of the coating mixture.
 82. A process for making a corrosion-resistant metal component coating as claimed in claim 66 wherein the step of applying the coating mixture solution further comprises filling any voids in the zinc or zinc-alloy surface with the coating mixture solution.
 83. A process for making a corrosion-resistant metal component coating as claimed in claim 66 wherein the step of applying the coating mixture solution further comprises filling any voids in the zinc or zinc-alloy surface with the coating mixture solution.
 84. A process for making a corrosion-resistant metal component coating as claimed in claim 66 wherein the corrosion-resistant metal component coating provides electrical conductivity.
 85. A process for making a corrosion-resistant metal component coating as claimed in claim 66 wherein the corrosion-resistant metal component coating is water-repellant.
 86. A process for making a corrosion-resistant metal component coating as claimed in claim 66 wherein the corrosion-resistant metal component coating provides an enhanced surface for a zinc or zinc-alloy coated metal component for adhesion to paints.
 87. A process for making a corrosion-resistant metal component coating as claimed in claim 66 wherein the corrosion-resistant metal component coating is self-healing. 